A) Ferromagnetic domains get perfectly arranged.
B) Ferromagnetic domains get randomly arranged.
C) Ferromagnetic domains are not at all influenced.
D) Ferromagnetic material transforms into diamagnetic substance.
Correct Answer: B
Solution :
Option (b) is correct. Explanation: On heating above Curie temperature. Ferromagnetic domains get randomly arranged and it transforms into paramagnetic substance.You need to login to perform this action.